TA18 titanium alloy is an advanced α-type titanium alloy with a nominal composition of Ti-3A12V. It was developed as a cold processable pipe material. At room temperature and high
At temperature, its strength is 209% -50% higher than pure titanium, and its welding performance and cold forming performance are better than TC4 alloy. The maximum operating temperature is about 315 ° C. Although the strength of this alloy is not as high as that of TC4 alloy, it has been widely used because of its excellent cold workability.
Product Description
| Product name | TA18 Ti 3Al2.5V Alloy Grade 9 Titanium Bar |
| Standard | ASTMB348/ASTM F67/ASTM F136 |
| Material | Pure titanium and titanium alloys |
| Advantages | 1. Resistance to acid and alkali corrosion, seawater corrosion and sewage corrosion 2. Low density, light weight 3. The non-magnetic 4. When used between -253-600°, its tensile strength is almost the highest among metals |
| Chemical compositions(weight%,<=) | ||||||||
| Main component | other | |||||||
| Ti | V | Fe | C | N | H | O | single | total |
| Remain | 1.5-3.0 | 0.25 | 0.08 | 0.05 | 0.015 | 0.12 | 0.10 | 0.30 |
| Physical properties(>=) | ||||||
| alloy composition | Σb Tensile Strength (Mpa) | σr0.2 Yield Strength (Mpa) |
ψ Elongation (%) | |||
| Ti 3Al2.5V | Ksi | Mpa | Ksi | Mpa | 15F | |
| 90 | 620 | 1010 | 13 | |||